HIGH TEMPERATURE CALCIUM SILICATE BOARD

HIGH TEMPERATURE CALCIUM SILICATE SLAB

HIGH TEMPERATURE CALCIUM SILICATE PIPE SECTION

HIGH TEMPERATURE CALCIUM SILICATE POWDER

Description: Non-asbestos EASTM HIGH TEMPERATURE calcium silicate heat-insulating products are nonpoisonous, tasteless, nondusty, and have the adcantages of light specific  gravity, high strength, small thermal conducttivity and convenience in laying. So that , they are largery  used in power, chemical, oil, gas, ship, steel and textile industries for the thermal insulatin of heating  power pipe and installations.Calcium silicate can be made into calcium silicate board(slab),pipe cover, calcium silicate powder, insulation cement, ect.
Technical Data Sheet of HT calcium silicate board and pipe section
Properties			Physical Index
Item		Unit	EASTM-HT	GB11835-89	JISA9510-1995	ASTM-C533 TYPE II	BS3958-82
Denisty		kg/m³	≤220	≤220	≤220	≤240	210-280
Maximum use temperature		℃	1100	650	1000	982	950
Thermal conductivity (At average 70±℃)			≤0.042	≤0.062	≤0.053	0.095 (240℃)	≤0.074 (200℃)
Bending strength		Mpa	≥0.45	≥0.3	≥0.31	≥0.31	≥0.25
Compressive strength		Mpa	>0.69	>0.5		≥0.414	≥0.35
Soaking heat Linear shrinkage (927℃  24h)		%	<2.0	≤2.0	<2.0	<2.0	<2.0
Moisture content		%	≤6	≤7.5			≤7.5
Non-Combustibility			ok
Fire resistance	Ignitability		0
	Spread of Flame		0
	Heat evolved		0
	Smoke developed		0
Standard size and packaging and Dimension tolerance
Class	Items	Sizes				Tolerances
Board (Slab)	Length (mm)		600, 610, 915, 1000			+3, -2
	Width (mm)		500, 300, 150			+3, -2
	Thickness (mm)		25---75---150			+3, -2
Pipe cover	Length (mm)		600, 610, 915			+3, -2
	Inside diameter (mm)		16---3560			+3, -2
	Thickness (mm)		25---75---150			+3, -2
Standard packaging		Polythene bags inside and Cardboard cartons outside
Technical Data Sheet of calcium silicate powder
Properties				Unit	Physical Index
Density				kg/m³	≤420
Maximum use temperature				℃	1100
Thermal conductivity (At average 50±℃)				W/m K	≤0.145
Compressive strength				Kpa	≥890
Linear shrinkage (923k  16h)				%	≤2.0